Flat Single Glass
LAMGLAS Skytec®
Single/Monolithic Glazing: Single
The exterior glass used in all PLANAR systems is normally (8+1+8)mm or (6+1+10)mm thick tempered and heat soaked glass that can be either clear or tinted. All glass complies with CE sertificated by SİSECAM. All glass, after tempering, must pass a destructive quality control test, the heat soak. This test is designed to virtually eliminate spontaneous on site breakage of glass due to the possible presence of nickel sulfide. Lamglas able to manufacturing all glass into a structural application which costumer prefered has heat soak.
Heat soaking is a prudent investment in safety for all those concerned about liability on a project.
Specification- flat single LAMGLAS Skytec®
FLAT SINGLE GLASS
Thickness: Tolerance:
10, 12mm +/-1mm
15mm +/- 1mm
19mm +/- 2mm
For dimensions
| LAMGLAS Skytec®Flat single glass size rectangles |
|
<2m |
<>/=2m |
| Maximum: |
1900 x 3900mm |
+/-1mm |
+/-2mm |
| Minimum: |
400 x 700mm |
+/-1mm |
+/-2mm |
| Aspect ratio: |
10:1 |
Maximum |
|
Diagonal tolerance:
Up to 4m: 3mm Maximum difference
Over 4m 4mm Maximum difference
Flat shape capability- simple shapes
All tolerances will vary depending on the complexity of shape.
Edge condition Smooth ground edges giving a flat profile with small ground arris. Shells or chips at edges will be ground out prior to toughening and do not constitute reason for rejection. Corners may be dubbed. Some variations in edgework may be discernible on exposed edges where different machines and/or hand forming is a requirement for manufacture. Such variations shall be kept to a minimum.
Hole drilling- rectangles
| Diameter: |
19mm +/-1mm (countersunk) |
| Position: |
Normally 100mm from glass edge at corners and sometimes along edge. Other configurations subject to confirmation. |
| Tolerance: |
+/-1mm from one datum point. |
| Number: |
2-8 |
Toughening stress
Fully toughened to BS 6206 Class A and equivalent international standards. Checked regularly during production by the Differential Surface Refractometer (DSR) method.
Heat soak testing
All toughening glass will be supplied heat soak tested to DIN Standard.
Glass marking
Glass will be marked with the LAMGLAS toughening stamp and any other regulatory requirements. The mark to be on each glass usually near a corner.